7475 T651 T7651 T7351 aircraft aluminum alloy sheet for Fuselage bulkheads
Alloy 7475 aluminum plates are a controlled toughness alloy whose values are 40 percent greater than alloy 7075 in the same tempers. This alloy’s corrosion resistance and fatigue behavior are also equal to, or better than, many of the other high strength aerospace alloys, and is for those applications that require a combination of high strength, superior fracture toughness and resistance to fatigue crack propagation.
The strength and corrosion resistance of the 7475 alloy are equivalent to those of the 7075 alloy at the same state, while the fracture toughness is higher than that of the existing aluminum alloy with equal strength. Its strength and fracture toughness match best.
The 7475 aluminum alloy sheet is supplied with O, T6 and T76, and the thick plate is supplied with T651, T7651 and T7351. Compared with the state of T76 and T6, the corrosion resistance, especially the anti peeling corrosion resistance, was improved, but the strength was reduced. Compared with the state of T7651 and T651, the resistance to peeling corrosion and stress corrosion resistance is improved, and the fracture toughness is improved, but the strength is reduced.
The technical standard of 7475 alloy not only stipulates the tensile properties at room temperature, but also stipulates the fracture toughness index. The 7475 T651 T7651 T7351 aluminum alloy sheet is mainly used for manufacturing high strength, medium fatigue strength and high fracture toughness structure, such as wing skin, fuselage skin and spacer. Using 7475 alloy can improve the safety, reliability and service life of the aircraft. As 7475 is a high strength aluminum alloy at room temperature, the strength properties of the alloy will be reduced with the increase of the temperature, and the long-term use temperature should not exceed 125 ℃.
XIAOXIAN RUIYI Can manufacture aluminum alloy plate sheet as
Alloy: 1050 1060 1100 3003, 3105, 5052, 5005, 5754 5083 5182, 6061 6063 6082, 7075, 8011…
Temper: HO, H111,H12, H14, H24,H 32, H112, T4, T6, T5,T651
Surface:Mill/Emboss/Diamond/2bar/3bars/Bright
Thickness: 0.2mm to 300mm
Width: 30mm to 2300mm
Length:1000mm to 10000mm.
Aluminium plate | aluminum alloy sheet | Aluminum tread plates | Aluminum coils | Aluminum Foils| Aluminium diamond plate sheet | Aluminum checker plates | Aluminium chequer plate sheet
| Chemical Analysis of aluminum alloy Plate | ||||||||||
| Alloy | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Al |
| 1050 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | - | - | 0.05 | 0.03 | Remains |
| 1060 | 0.25 | 0.35 | 0.05 | 0.03 | - | - | - | - | - | Remains |
| 1070 | 0.2 | 0.25 | 0.04 | 0.03 | 0.03 | - | - | - | - | Remains |
| 1100 | 0.95 | 0.95 | 0.05-0.2 | 0.05 | - | - | 0.1 | - | - | Remains |
| 1200 | 1 | 1 | 0.05 | 0.05 | - | - | - | 0.1 | 0.05 | Remains |
| 3003 | 0.6 | 0.7 | 0.05-0.2 | 1.0-1.5 | - | - | - | 0.1 | - | Remains |
| 5005 | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | - | 0.25 | - | Remains |
| 5042 | 0.2 | 0.35 | 0.15 | 0.2--.5 | 3.0-4.0 | 0.1 | - | 0.25 | 0.1 | Remains |
| 5052 | 0.25 | 0.4 | 0.1 | 0.1 | 2.2-2.8 | 0.15-0.35 | - | 0.1 | - | Remains |
| 5083 | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | - | 0.25 | - | Remains |
| 5754 | 0.4 | 0.4 | 0.1 | 0.5 | 2.6-3.6 | 0.3 | - | 0.2 | - | Remains |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | - | 0.25 | - | Remains |
| 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45 | 0.1 | - | 0.1 | - | Remains |
| 6082 | 0.7-1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6-1.2 | 0.25 | - | 0.2 | - | Remains |
| 7050 | 0.12 | 0.15 | 2.0-2.6 | 0.1 | 1.9-2.6 | 0.04 | - | 5.7-6.7 | 0.06 | Remains |
| 7075 | 0.4 | 0.5 | 1.2-2.0 | 0.3 | 2.1-2.9 | 0.18-0.28 | - | 5.1-6.1 | 0.2 | Remains |